Stainless Steel 430 Cold Finish SS Wire Rod UNS S43000 Diameter 0.8-15mm

Contact Now
Ningbo Huayuan Metal Products Co., Ltd.
City:ningbo
Province/State:zhejiang
Country/Region:china
Contact Person:MrZhou
Contact Now

Stainless Steel 430 Cold Finish SS Wire Rod UNS S43000 Diameter 0.8-15mm

Ask Latest Price
Video Channel
Brand Name :Toponewire
Model Number :0.8-18mm
Certification :ISO9001:2015
Place of Origin :China
MOQ :500KG
Price :USD 1-5 Per KG
Payment Terms :D/P, Western Union, L/C, T/T, , D/A
Supply Ability :>500 tons per month
Delivery Time :1-15 days
Packaging Details :coil or spool with plate.
Material :430/410
diameter :0.8-15mm
packing :by customer request
Standard :JIS G. EN. ASTM. DIN. GB etc
surface :matt or bright
Surface :Bright,Matte
Length :Customer Request
more
Contact Now

Add to Cart

Find Similar Videos
View Product Description

Stainless Steel 430 Cold Finish Wires, SS UNS S43000 Wire Rods

Why use this magnetic stainless steel?

Stainless steel grade 430 is a non-hardenable steel containing straight chromium, and belongs to the ferritic group of steels.

Stainless steel grade 430 is capable of resisting oxidation up to 870°C (1598°F) in intermittent usage, and up to 815°C (1499°F) in continuous usage. At room temperature, it has the tendency to become brittle, especially when it has been heated for a long time in the 400-600°C (752-1112°F) range. This issue can be overcome with annealing.

Solution annealing can be performed by heating stainless steel grade 430 to 815 - 845°C (1499-1553°F). Then it has to be slow furnace cooled to 600°C (1112°F) and followed by air-cooling in a quick manner - as slow cooling between 540 and 400°C (1004 and 752°F) tends to cause embrittlement.

For sub-critical annealing, heating should be performed to 760-815°C (1400-1499°F), followed by air-cooling or water quenching.
This stainless steel cannot be hardened by thermal treatment.

Dimensions of Wire:

Diameter – 0.255mm (255 Micron – 31 AWG)
Length – Various Options
Weight – Various Options
Spool Type – Large plastic bobbin.

Technical Specification:

Ohms/m – 11.75

Chemical Composition:
Fe, <0.12% C, 16-18% Cr, <0.75% Ni, <1.0% Mn, <1.0% Si, <0.040% P, <0.030% S

C Min - - Max - 0.12
Mn Min - - Max - 1
Si Min - - Max - 1
P Min - - Max - 0.04
S Min - - Max - 0.30
Cr Min - 16 Max - 0.18
Mo Min - - Max - -
Ni Min - - Max - 0.50
N Min - - Max - -

Tensile Str (MPa) - 483
Yield Str 0.2% - Proof (MPa) Min - 310
Elong (% 50mm)) Min - 22
Hardness - Rockwell B (HR B) Max - 85
Brinell (HB) Max - 183
Density (kg/m3) - 7750
Elastic Modulus (GPa) - 200
Mean Co-eff of Thermal Expansion (µm/m/°C) 0-100°C - 10.4 0-315°C - 11 0-538°C - 11.4
Thermal Conductivity (W/m.K) - At 100°C - 26.1 At 500°C - 26.3
Specific Heat 0-100°C (J/kg.K) - 460
Elec Resistivity (n?.m) - 600